Effect of addition titanium dioxide nanoparticles as acrylic resin denture base filler on cytotoxicity

https://doi.org/10.22146/majkedgiind.38438

Ardhianing Hardita(1), Titik Ismiyati(2), Endang Wahyuningtyas(3*)

(1) Klinik Gigi Dhea, Yogyakarta Prostodontics Specialty Study Program, Faculty of Dentistry, Universitas Gadjah Mada, Yogyakarta
(2) Department of Prosthodontics, Faculty of Dentistry, Universitas Gadjah Mada, Yogyakarta
(3) Department of Prosthodontics, Faculty of Dentistry, Universitas Gadjah Mada, Yogyakarta
(*) Corresponding Author

Abstract


Denture base material should have a good level of biocompatibility. Acrylic resin is frequently used as a denture base material, however it has a disadvantage of producing residual monomer. Residual monomer is known to have a cytotoxicity effect. Titanium dioxide (TiO2) nanoparticles are used as fillers due to their biocompatibility and ability to enhance the mechanical properties of acrylic resin. The addition of the material to acrylic resin could affect the amount of residual monomer. The aim of this study was to examine the effect of the addition of TiO2 nanoparticles as acrylic resin denture base filler on the cytotoxicity in fibroblast cells. The samples consisted of 24 heat cured acrylic resins in disc shape (5 mm in diameter and 2 mm in thickness), divided into 4 groups (n = 6): three groups given treatment with
0.5%, 1%, 2% TiO2, respectively and one control group. Cell viability was measured with MTT assay. The results were tested with one way ANOVA with 95% confidence level followed by LSD post hoc test. The results showed that the highest percentage of cell viability was found in the treatment group of 0.5% TiO2 with value of 91.83 ± 1.75%, while the lowest value was seen in the treatment group of 2% TiO2 with value of 79.38 ± 3.34%. Significant differences were shown between the treatment groups of 0.5% and 2% TiO2, as well as between the control and treatment group with 2% TiO2. The conclusions of this research are the addition of TiO2 nanoparticles as acrylic resin denture base filler has an effect on cytotoxicity; the addition of 0.5% TiO2 nanoparticles filler results in lower cytotoxicity on fibroblast cells compared to the addition of 1% and 2% TiO2.










 

 


Keywords


acrylic resin denture base; cytotoxicity; fibroblast cell; titanium dioxide nanoparticles

Full Text:

PDF


References

1. Gunadi HA, Margo A, Burhan LK, Sutyatenggara F, Setiabudi I. Buku ajar ilmu
gigi tiruan sebagian lepasan Jilid I. Jakarta: Hipokrates; 2013. 11-12.


2. McCabe, John F. Applied dental material. 9th ed. Oxford: Blackwell Publishing Ltd; 2008.
110-123.


3. Vojdani M, Giti R. Polyamide as a denture base material a literature review. J Dent Shiraz
UnivMed Sci. 2015; 16(1): 1-9.


4. Mallikarjuna AV. Cytotoxicity of acrylic resin: a review. IOSR-JDMS. 2014; 13(3): 07-09.
doi: 10.1016/s0022-3913(03)00349-4

5. Salman TA. The influence of adding modified ZrO2-TiO2 nanoparticles on certain physical and mechanical properties of heat polymerized acrylic resin. J Bagh College Dentistry. 2015; 27(3): 33-39. doi: 10.12816/0015032


6. Ahmed MA. Effect of titanium dioxide nano particles incorporation on mechanical and physical properties on two different types of acrylic resin denture base. WJNSE. 2016; 6: 111-119. doi: 10.4236/wjnse.2016.63011


7. Allen R. The cytotoxic and genotoxic potential of titanium dioxide (TiO2) nanoparticles on
human SH-SY5Y neuronal cells in vitro. PSS. 2016; 9(2): 5-28.

8. Shirkavand S. Effect of TiO2 nanoparticles on tensile strength of dental acrylic resins. JODDD. 2014; 8(4): 197-203. doi: 10.5681/joddd.2014.036


9. Zhu X, Hondroulis E, Liu W, Li C. Biosensing approaches for rapid genotoxicity and cytotoxicity assays upon nanomaterial exposure, Small. 2013; 9: 1821-1830. doi: 10.1002/smll.201201593

10. Alwan SA, Alameer SS. The effect of the addition of silanized nano titania fillers on some physical and mechanical properties of heat cured acrylic denture base materials. J Bagh Coll Dentistry. 2015; 27(1): 86-91.

11. Saravi ME. Evaluation of cellular toxicity of three denture base acrylic resins. J Dent (Tehran). 2012; 9(4): 180-188.

12. Heravi F, Ramezani M, Poosti M, Hosseini M, Shajiei A, Ahrari F. In vitro cytotoxicity assessment of an orthodontic composite containing titanium-dioxide nano-particles. J Dent Res. 2013; 7(4): 192–198. doi: 10.5681/joddd.2013.031

13. Shin-etsu. Silane coupling agent, Japan Tokyo: Shin-Etsu Chemical Co Ltd; 2017. 1-28.

14. Anusavice KJ, Shen C, Rawls HR. Phillip’s science of dental materials. 12th ed. USA: Elsevier; 2013. 493-494.

15. Ammerman NC, Beier-Sexton M, Azad AF. Growth and maintenance of vero cell lines, Curr Protoc Microbiol, APPENDIX. Appendix-4E; 2008.

16. ISO 10993-5. Biological evaluation of medical devices — Part 12: Sample Preparation and
Reference Materials. Switzerland: ISO. 2012; 2012. 24-28

17. Shibata T, Hamada N, Kimoto K. Antifungal effect of acrylic resin containing apatite-coated
TiO2 photocatalyst, Dent Mater J. 2007; 26(3): 437-44. doi: 10.4012/dmj.26.437

18. Chen R, Han Z, Huang Z, Karki J, Wang C, Zu B, Zhang X. Antibacterial activity, cytotoxicity and mechanical behavior of nano-enhanced denture base resin with different kinds of inorganic
antibacterial agents. Dent Mater J. 2017; 36(6): 693-699. doi: 10.4012/dmj.2016-301

19. Tadano T, Rui Z, Yoshio M, Toru H, Shoichiro Y. A new mechanism for the silica nanoparticle
dispersion–agglomeration transition in a poly(methyl methacrylate)/silica hybrid suspension, Polymer Journal. 2014; 46: 342–348. doi: 10.1038/pj.2014.6

20. Nazirkar G, Bhanushali S, Singh S, Pattanaik B, Raj N. Effect of anatase titanium dioxide
nanoparticles on the flexural strength of heat cured poly methyl methacrylate resins: an invitro
study. J Indian Prosthodont Soc. 2014; 14(1): 144–149. doi: 10.1007/s13191-014-0385-8

21. Silva CRC, Pellissari CV, Sanitá PV, Amaya MI, Masetti P, Jorge JH. Metabolism of L929
cells after contact with acrylic resins. Part 1: acrylic denture base resins. Int J Dentistry Oral Sci. 2015; S1(001): 1-5. doi: 10.19070/2377-8075-SI01001

22. Chaves CAL, Machado AL, Carlos IZ, Giampaolo ET, Pavarina AC, Vergani CE.
Cytotoxicity of monomers, plasticizer and degradation by-products released from dental
hard chairside reline resins. Dent Mater. 2010; 26(10): 1017-1023. doi: 10.1016/j.dental.2010.06.008



DOI: https://doi.org/10.22146/majkedgiind.38438

Article Metrics

Abstract views : 3396 | views : 2276

Refbacks

  • There are currently no refbacks.




Copyright (c) 2019 Majalah Kedokteran Gigi Indonesia

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.


 

 View My Stats


real
time web analytics