The Effects of Withdrawal Stop Duration in the Directional Solidification of Al-7 wt% Si Alloy on Solidification Parameters, Microstructure, and Microhardness

https://doi.org/10.22146/jmpc.52249

Seab Piseth(1*), Dedy Masnur(2)

(1) Department of Industrial and Mechanical Engineering, Faculty of Electrical Engineering, Institute of Technology of Cambodia, Russian Federation Boulevard P.O. BOX 86 Phnom Penh, Cambodia
(2) Mechanical Engineering Department, University of Riau, Kampus Bina Widya km 12.5 Simpang Baru, Pekanbaru 28293, Indonesia
(*) Corresponding Author

Abstract


The effects of withdrawal stop duration in the directional solidification of Al-7 wt% Si alloy on solidification parameters, microstructure, and microhardness were investigated. Directional solidification experiments were carried out in five stopping durations: 0 s, 20 s, 30 s, 40 s, and 50 s. Some solidification parameters such as growth rate and temperature gradient were calculated in the stopping region 15 mm from the bottom of the sample. Microstructure parameters such as primary and secondary dendrite arm spacings were defined on both longitudinal and transverse sections in the stopping region, whereas microhardness properties were tested on the longitudinal section in this region. With the rise in the withdrawal stop duration from 0 s to 50 s, the growth rate decreased slightly from 1.26 to 0.84 mm/s, while the temperature gradient remained at 1.71 ˚C/mm. Furthermore, the microstructure of α-Al dendrites became coarser, and their shapes changed from thin to irregular plates. Primary and secondary dendrite arm spacings increased from 106.4 to 205.7 µm and 19.4 to 38.1 µm, respectively, when the stopping duration was increased. In addition, the hardness decreased from 54.0 to 49.9 HV.

Keywords


Aluminum alloys, Dendrite growth, Directional solidification, Withdrawal

Full Text:

PDF


References

D. M. Stefanescu, Science and engineering of casting solidification, Third Edit. SpringerInternational Publishing Switzerland 2015, 2009.

F. C. Robles-Hernandez, J. M. H. Ramírez, and R. Mackay, Al-Si Alloys. 2017.

H. Kaya and A. Aker, “Effect of alloying elements and growth rates on microstruture and mechanical properties in the directionally solidified Al-Si-X alloys,” J. Alloys Compd., vol. 694, pp. 145–154, 2017.

H. Kaya, E. Çadirli, and M. Gündüz, “Dendritic growth in an aluminum-silicon alloy,” J. Mater. Eng. Perform., vol. 16, no. 1, pp. 12–21, 2007.

H. Kaya, E. Çadirli, M. Gündüz, and A. Ülgen, “Effect of the temperature gradient, growth rate, and the interflake spacing on the microhardness in the directionally solidified Al-Si eutectic alloy,” J. Mater. Eng. Perform., vol. 12, no. 5, pp. 544–551, 2003.

H. Zhong et al., “Effect of interdendritic thermoelectric magnetic convection on evolution of tertiary dendrite during directional solidification,” J. Cryst. Growth, vol. 439, pp. 66–73, 2016.

J. Campbell, Complete Casting, First edit. Elsevier, 2011.

J. G. Kaufman and E. L. Rooy, Aluminum Alloy Castings: Properties , Processes , and Applications. 2004.

J. R. Davis, “Aluminum and Aluminum Alloys,” in ASM International, 2001, pp. 351–416.

K. G. Basavakumar, P. G. Mukunda, and M. Chakraborty, “Influence of grain refinement and modification on microstructure and mechanical properties of Al-7Si and Al-7Si-2.5Cu cast alloys,” Mater. Charact., vol. 59, no. 3, pp. 283–289, 2008.

M. Gupta and S. Ling, “Microstructure and mechanical properties of hypo/hyper-eutectic Al-Si alloys synthesized using a near-net shape forming technique,” J. Alloys Compd., vol. 287, no. 1–2, pp. 284–294, 1999.

M. Okayasu and S. Takeuchi, “Crystallization characteristics of cast aluminum alloys during a unidirectional solidification process,” Mater. Sci. Eng. A, vol. 633, pp. 112–120, 2015.

M. Şahin and E. Çadirli, “The effects of temperature gradient and growth rate on the microstructure of directionally solidified Sn-3.5Ag eutectic solder,” J. Mater. Sci. Mater. Electron., vol. 23, no. 2, pp. 484–492, 2012.

N. Maraşli, K. Keşlioǧlu, B. Arslan, H. Kaya, and E. Çadirli, “Effects of growth rate and temperature gradient on the microstructure parameters in the directionally solidified succinonitrile-7.5 wt.% carbon tetrabromide alloy,” J. Mater. Process. Technol., vol. 202, no. 1–3, pp. 145–155, 2008.

S. Engin, U. Büyük, and N. Maraşli, “The effects of microstructure and growth rate on microhardness, tensile strength, and electrical resistivity for directionally solidified Al-Ni-Fe alloys,” J. Alloys Compd., vol. 660, pp. 23–31, 2016.

S. Steinbach and L. Ratke, “The influence of fluid flow on the microstructure of directionally solidified AlSi-base alloys,” Metall. Mater. Trans. A, vol. 38 A, no. 7, pp. 1388–1394, 2007.

U. Böyük, S. Engin, and N. Maraşli, “Microstructural characterization of unidirectional solidified eutectic Al-Si-Ni alloy,” Mater. Charact., vol. 62, no. 9, pp. 844–851, 2011.

W. Rasband, “Downloads - ImageJ,” 2018. [Online]. Available: https://imagej.net/Downloads. [Accessed: 12-Apr-2019].

Y. Kaygısız and N. Maraşlı, “Directional solidification of Al–Cu–Si–Mg quaternary eutectic alloy,” J. Alloys Compd., vol. 721, pp. 764–771, 2017.

Y. Koçak, S. Engin, U. Böyük, and N. Maraşlı, “The influence of the growth rate on the eutectic spacings, undercoolings and microhardness of directional solidified bismuth–lead eutectic alloy,” Curr. Appl. Phys., vol. 13, no. 3, pp. 587–593, 2013.



DOI: https://doi.org/10.22146/jmpc.52249

Article Metrics

Abstract views : 1452 | views : 1202

Refbacks

  • There are currently no refbacks.